      機械用碳石墨材料類別/型號及技術性能

      作者:http://www.aspxcool.com 發布時間:2022-03-25 20:31:29

      機械用碳石墨材料類別/型號及技術性能

      機械用碳石墨材料類別/型號及技術性能

      型號
      Type 
      浸漬材料
      Impregnated Material
      體積密度 BulkDensity 

      g/cm3 (≥)
      抗折強度
      Transverse Strength Mpa(≥)
      抗壓強度
      Conpressive Strength
      Mpa (≥)
      肖氏硬度 Hardness Shore
      (≥)
      氣孔率% Porosity

      (≤)
      熱膨脹系數
      Coeffcient of Expansion X10-6 /℃
      使用溫度℃
      Nax.Suitable Temperature
      碳石墨 Pure Carbon Graphite
      XH-M191純碳石墨1.7585150901.2600
      XH-M126碳石墨(T)1.60401006512.0400
      XH-M2541.7025454020.0450
      XH-M2381.7035754015.0450
      浸漬樹脂石墨 Resin-Impregnated Graphite
      XH-M106H環氧樹脂
      Epoxy Resin
      (H)
      1.7565200851.5210
      XH-M120H1.7060200851.5
      XH-M126H1.7055160801.5
      XH-M180H1.8080220901.5
      XH-M254H1.803575421.5
      XH-M238H1.8850105551.5
      XH-M106K呋喃樹脂
      Furan Resin
      (k)
      1.7565200901.5210
      XH-M120K1.7060200851.5
      XH-M126K1.7060170851.5
      XH-M180K1.8080220901.5
      XH-M238K1.8555105551.5
      XH-M254K1.804080451.5
      XH-M180F酚醛樹脂
      Phenolic Resin
      (F)
      1.8070220901.5210
      XH-M106F1.7560200851.5
      XH-M120F1.7055190801.0
      XH-M126F1.7050150751.5
      XH-M238F1.8850105551.5
      XH-M254F1.803575451.0
      浸漬金屬石墨 Metal-Impregnated Graphite
      XH-M120B巴氏合金
      Babbitt
      (B)
      2.4060160659.0210
      XH-M254B2.404070408.0
      XH-M106D銻  Antimony (D)2.2075190702.5400
      XH-M120D2.2070180652.5
      XH-M254D2.204085402.5450
      XH-M106P銅合金 Copper Alloy    (P)2.6070240703.0400
      XH-M120P2.4075250753.0
      XH-M254P2.6040120453.0450
      樹脂粘合石墨 Resin Graphite
      XH-301熱壓石墨1.705098621.0200
      XH-302熱壓石墨1.6555105581.0180